Pengaruh Variasi Jenis Pelarut Dan Jenis Cat Sebagai Inhibitor Korosi Terhadap Laju Korosi Baja Astm A36
DOI:
https://doi.org/10.51903/juritek.v6i1.6521Keywords:
Baja ASTM A36, Korosi, Pelapisan Cat, Thinner, Laju KorosiAbstract
This study aims to analyze the effect of solvent variations in paint mixtures on the corrosion rate of ASTM A36 steel in a seawater immersion environment. ASTM A36 steel is widely used in construction and marine structures but is susceptible to corrosion due to exposure to seawater containing high concentrations of chloride ions. One commonly applied method for corrosion control is surface coating using paint as a physical inhibitor, whose effectiveness is strongly influenced by the type of solvent used. The solvent variations investigated in this study include thinner A special, thinner A ordinary, and thinner B. The research employed a quantitative experimental method. ASTM A36 steel specimens were coated with paint using a 50:50 ratio of paint to solvent and then immersed in natural seawater for 30 days. The corrosion rate was determined using the weight loss method. In addition, surface morphology observations after immersion were conducted using an optical microscope to identify the type and severity of corrosion damage. The results indicate that variations in solvent type within the paint mixture affect the corrosion rate of ASTM A36 steel. Certain combinations of paint and solvent were able to reduce the corrosion rate more effectively than others. These differences are attributed to the solvent’s ability to form a protective coating with good adhesion and uniformity on the steel surface. Therefore, selecting an appropriate solvent type can enhance the effectiveness of paint coatings as a corrosion control method for ASTM A36 steel in marine environments.
References
[1] J. R. Material and M. Energi, “Jurnal Rekayasa Material, Manufaktur dan Energi,” vol. 8, no. 2, pp. 405–410, 2025.
[2] A. F. Ridho and I. N. Rokhim, “E -ISSN : 2746-0835 Volume 4 No 3 ( 2023 ) JUSTI ( Jurnal Sistem Dan Teknik Industri ) ANALISIS TEKNIS DAN EKONOMIS KOROSI PERBANDINGAN ASTM A36 DAN ALUMINIUM 5083 UNTUK PELAT KAPAL E -ISSN : 2746-0835 Volume 4 No 3 ( 2023 ) JUSTI ( Jurnal Sistem Dan Tekn,” vol. 4, no. 3, 2023.
[3] A. Haslinah, “MENGGUNAKAN VARIASI AIR LAUT,” vol. 20, no. April, pp. 51–56, 2025.
[4] D. S. Rabbani, Analisis Laju Korosi Dan Sifat Mekanik Pada Material Baja Astm a36 Untuk Rotor Bezier-Savonius Dengan Media Air Laut. 2025. [Online]. Available: https://eprints.untirta.ac.id/id/eprint/48999
[5] A. Coating, D. A. N. Tanpa, and C. Baja, “Jurnal teknik perkapalan,” vol. 12, no. 2, pp. 1–12, 2024.
[6] S. Risqi, A. Rani, and K. Abidin, “PENGARUH PENAMBAHAN INHIBITOR ALAMI EKSTRAK LIMBAH KULIT JAGUNG TERHADAP LAJU KOROSI MATERIAL BAJA ST 37 DALAM MEDIUM NaCl 3%,” pp. 116–127.
[7] F. A. Noormansyah, S. Jokosisworo, and W. Amiruddin, “Analisis pengaruh salinitas terhadap laju korosi merata baja ss 400 dengan variasi ketebalan coating,” Tek. Perkapalan, vol. 7, no. 2, pp. 152–160, 2023.
[8] A. B. Aji, A. W. B. Santosa, and I. P. Mulyatno, “Analisa Pengaruh Variasi Ketebalan Serta Jenis Coating Pada Pelat Baja SS400 Terhadap Laju Korosi dan Uji Adhesi,” J. Tek. Perkapalan, vol. 12, no. 2, pp. 1–9, 2024, [Online]. Available: https://ejournal3.undip.ac.id/index.php/naval
[9] P. Pendidikan, P. Insinyur, U. K. Petra, and J. S. Setiadji, “Aplikasi Katodik Proteksi Dengan Sistem Anoda Korban Untuk Mencegah Korosi Pada Pipa Logam,” vol. 3, pp. 9–15, 2025.
[10] L. Nacl, “STUDY OF NaNO 2 INHIBITORS AS CORROSION CONTROL RATE OF STAINLESS STEEL IN NaCl 3 . 5 % ENVIRONMENT”.
[11] P. Asam, S. Organik, P. Korosi, B. Tahan, K. Tinjauan, and R. K. Suleiman, “logam,” 2023.
[12] Y. Zhu, J. Wang, H. Liu, P. Ren, and F. Yan, “Effect of Dissolved Oxygen Content on Tribo-Corrosion Behavior of Monel 400 Alloy in Seawater,” Metals (Basel)., vol. 14, no. 1, 2024, doi: 10.3390/met14010006.
[13] T. Natasya, M. E. Khairafah, M. Sari, B. Sembiring, and L. Nazrifah, “Indonesian Journal of Chemical State University of Medan,” 2022.
[14] E. López-Baltazar, R. González-Parra, A. Barba, and M. Á. Hernández Gallegos, “Effects of hydrostatic pressure and temperature on the corrosion behavior of X52 pipeline steel in a simulated deep-sea environment,” Discov. Electrochem., vol. 2, no. 1, 2025, doi: 10.1007/s44373-025-00025-x.
[15] J. Jefrimon, L. G. Marni, I. Noviarni, and R. Safitri, “Penggunaan Ekstrak Biji Alpukat (Persea americana) sebagai Inhibitor Korosi pada Baja Tahan Karat,” J. Kolaborasi Sains dan Ilmu Terap., vol. 2, no. 2, pp. 28–37, 2024, doi: 10.69688/juksit.v2i2.29.
[16] N. A. Mufarida and A. Abidin, “Quality of Fuel Liquid Waste Biogas Tofu Using Starter Composition Variation,” vol. 5, no. 2, pp. 17–21, 2020, doi: 10.21070/rem.v5i2.1001.
[17] D. Afrilia and S. Bahri, “INHIBITOR TERHADAP LAJU KOROSI PADA BAJA,” vol. 4, no. April, pp. 111–120, 2022.
[18] Nelvi Helmania Putri, Siska Dwi Febryani, Rabena Aprilla, and Hilfi Pardi, “Analisis Pengaruh Sifat Kimia Air Laut Terhadap Korosi Logam Dan Pengendaliannya Menggunakan Proteksi Katodik,” J. Res. Educ. Chem., vol. 6, no. 1, p. 34, 2024, doi: 10.25299/jrec.2024.vol6(1).17173.
[19] S. T. Mesin, F. Teknik, U. N. Surabaya, J. T. Mesin, F. Teknik, and U. N. Surabaya, “PENGARUH PERBANDINGAN CAMPURAN CAT DENGAN THINNER TERHADAP KUALITAS HASIL PENGECATAAN Nico Johansyah Habibie Saiful Anwar Abstrak,” pp. 97–104, 2021.
[20] A. Kekuatan et al., “Strength Analysis of Material Steel S45C on the Arm and Cantilever Shaft Rear Disc Brake Planning,” vol. 3, no. 1, pp. 2–5, 2018.
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Jurnal Ilmiah Teknik Mesin, Elektro dan Komputer
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
.png)